SheetOPTIX-L Colored

Continuous cast acrylic made with Lucite® monomer for superior clarity. OPTIX-L gives designers and fabricators excellent aesthetics, ultimate flexibility and craze resistance.

  • Thickness 0.118” – 0.22”
  • Width 48.0” – 108.0”
  • Length 96.0” – 108.25”
  • Translucent
  • Opaque
  • Indoor
  • Outdoor
Available Colors Custom colors available.
  • White
  • Black - 2025
  • Lighting-Panels_White
  • White - 7328
  • White - 3015
  • White - 2447
  • Bronze - 2412

*Colors on screen may not reflect exact matches to physical sheets.

*Non-Stock colors, patterns or sizes may require a minimum quantity order.

Features & Benefits

High molecular weight for ease of fabrication, uniform thickness and superior craze resistance

Chemical resistance; perfect for cosmetics displays

Exceptional UV stability, easy to shape, form, cut and bond

Ideal for retail/POP displays, interior design, picture framing, furniture and jewelry

ITEM # COLORS PATTERN/TEXTURES MASKING THICKNESS (in.) SIZE (in.) SQ FT PACK QTY SKID QTY REQUEST
180760 White - WT7328 F2 – 2 sided clear polyfilm masking 0.118 48.0” x 96.0” 32 80
180775 Black - BK2025 F2 – 2 sided clear polyfilm masking 0.118 48.0” x 96.0” 32 80
181099 Bronze - BZ2412 F2 – 2 sided clear polyfilm masking 0.118 108.0” x 108.25” 81.2 35
181100 White - WT2447 F2 – 2 sided clear polyfilm masking 0.118 108.0” x 108.25” 81.2 35
181885 White - WT7328 F2 – 2 sided clear polyfilm masking 0.118 108.0” x 108.25” 81.2 35
181889 Black - BK2025 F2 – 2 sided clear polyfilm masking 0.118 108.0” x 108.25” 81.2 35
181901 White - WT2447 F2 – 2 sided clear polyfilm masking 0.118 48.0” x 96.0” 32 80
183617 White - WT3015 F2 – 2 sided clear polyfilm masking 0.118 48.0” x 96.0” 32 80
180761 White - WT7328 F2 – 2 sided clear polyfilm masking 0.177 48.0” x 96.0” 32 55
181045 Bronze - BZ2412 F2 – 2 sided clear polyfilm masking 0.177 108.0” x 108.25” 81.2 25
181101 White - WT2447 F2 – 2 sided clear polyfilm masking 0.177 108.0” x 108.25” 81.2 25
181893 White - WT7328 F2 – 2 sided clear polyfilm masking 0.177 108.0” x 108.25” 81.2 25
185612 Black - BK2025 F2 – 2 sided clear polyfilm masking 0.177 108.0” x 108.25” 81.2 25
187140 White - WT3015 F2 – 2 sided clear polyfilm masking 0.177 48.0” x 96.0” 32 55
181068 White - WT7328 F2 – 2 sided clear polyfilm masking 0.22 48.0” x 96.0” 32 45
181130 Black - BK2025 F2 – 2 sided clear polyfilm masking 0.22 48.0” x 96.0” 32 45

Thermal

TEST METHOD

UNITS

OPTIX-L

Flame Spread Index

ASTM E-84

140

Smoke Density Rating

ASTM D-2843

%

13.5

Deflection Temperature @ 264 psi (1.8 MPa)

ASTM D-648

°F

200

Coefficient of Thermal Expansion

ASTM D-696

in/(in-°F ) x 10-5

3.5 E-05 in/in/˚F

Self-Ignition Temperature

ASTM D-1929

°F

750˚F

Forming Temperature

°F

280˚- 340˚F (138˚- 170˚C)

Thermal Conductivity

ASTM C-177

BTU-ft/(hr-ft2-°F)

1.45 Btu in/ft^2 hr. ˚F

Maximum Recommended Continuous Service Temperature

°F

175

Mechanical

TEST METHOD

UNITS

OPTIX-L

Dielectric Contstant @1mHz

ASTM D-150

2.7

Flexural Modulus of Elasticity

ASTM D-790

psi

461,000

Compressive Strength

ASTM D-695

psi

83,300

Dielectric Constant @1kHz

ASTM D-150

3

Shear Strength

ASTM D-732

psi

11,200

Volume Resistivity

ASTM D-257

ohms/cm

>3.912E+15 Ώ/cm

Flexural Strength

ASTM D-790

psi

14,700

Tensile Modulus of Elasticity

--

psi

465,000

Rockwell Hardness

ASTM D-785

M-100

Tensile Strength

ASTM D-638

psi

11,000

Dielectric Strength

ASTM D-149

volts/mil

354

Physical

TEST METHOD

UNITS

OPTIX-L

Light Transmission -Total

ASTM D-1003

%

92%

Water Absorption

ASTM D-570

% By wt

0.2

Light Transmission - Haze

ASTM D-1003

%

Less Than 1%

Optical Refractive Index

ASTM D-542

1.49

Specific Gravity/Relative Density

ASTM D-792

1.19

Download

**Applicable to the acrylic substrate

These suggestions and data are based on information we believe to be reliable. They are offered in good faith, but without guarantee, as conditions and methods of use are beyond our control. We recommend that the prospective user determine the suitability of our materials and suggestions before adopting them on a commercial scale.