PolymersCA-1000 E-2

Impact-modified grade polymer with high impact resistance designed for extrusion process. The typical applications are films, extruded sheets, capping material for other plastic substrates.

  • UL-94 HB
  • Impact Modified

Other

TEST METHOD

UNITS

CA-1000 E-2

Relative Thermal Index

UL 746 ABC

°C

90,f1

Flammability

UL 94

-

HB

Specific Gravity

ASTM D792

-

1.16

Thermal

TEST METHOD

UNITS

CA-1000 E-2

Molding Shrinkage

ASTM D955

%

0.2-0.6

Vicat Softening Temperature

ASTM D1525

°F

227

Melt Flow Rate

ASTM D1238

g/10 min

0.8

Coefficient of Linear Thermal Expansion (-30 to 30°C)

ASTM D696

mm/(mm-oC)

12 X 10^-5

Heat Deflection Temperature Under Load (264 psi)

ASTM D648

°F

176

Mechanical

TEST METHOD

UNITS

CA-1000 E-2

Impact Strength – Falling Weight (1/8”)

ASTM D5420 GB

in-lb

56

Tensile Strength

ASTM D638

psi

6510

Elongation

ASTM D638

%

38

Modulus of Elasticity

ASTM D638

psi

255000

Impact Strength – Izod (Notched)

ASTM D256

ft-lb/in

1.2

Flexural Strength

ASTM D790

psi

8890

Optical

TEST METHOD

UNITS

CA-1000 E-2

Refractive Index

ASTM D542

-

1.49

Luminous Transmittance

ASTM D1003

%

90.7

Haze

ASTM D1003

%

< 2

Yellowness Index

ASTM D1925

-

< 1.0

Download

**Applicable to the acrylic substrate

These suggestions and data are based on information we believe to be reliable. They are offered in good faith, but without guarantee, as conditions and methods of use are beyond our control. We recommend that the prospective user determine the suitability of our materials and suggestions before adopting them on a commercial scale.