SheetOPTIX Patterned Acrylic

OPTIX Patterned Acrylic sheet is a great choice to bring interesting and beautiful patterns to Shower Doors, displays indoor/outdoor furniture, and home furnishing products. OPTIX Patterned Acrylic is stocked in Adobe and P-32/Haircell patterns. Available in a variety of sheet sizes.

  • Thickness 0.22” – 0.22”
  • Width 43.0” – 48.5”
  • Length 43.0” – 46.5”
  • Translucent
  • Indoor
  • Outdoor
Available Colors Custom colors available.
  • Clear

*Colors on screen may not reflect exact matches to physical sheets.

*Non-Stock colors, patterns or sizes may require a minimum quantity order.

Features & Benefits

Custom sizes, thicknesses and colors available

ITEM # COLORS PATTERN/TEXTURES MASKING THICKNESS (in.) SIZE (in.) SQ FT PACK QTY SKID QTY REQUEST
635000-1 Clear Adobe No Masking 0.22 43.0” x 43.0” 12.8 45
P324896A Clear P-32 Wothington/Haircell Polyfilm 0.22 48.5” x 46.5” 15.7 50

Thermal

TEST METHOD

UNITS

OPTIX Patterned Acrylic

Flame Spread Index

ASTM E-84

115

Flammability (Burning Rate)

ASTM D-635

In/minute

1.019

Melting Temperature

°F

300-315

Coefficient of Thermal Expansion

ASTM D-696

in/(in-°F ) x 10-5

3.0

Self-Ignition Temperature

ASTM D-1929

°F

833

Deflection Temperature @ 264 psi (1.8 MPa)

ASTM D-648

°F

203

Smoke Density Rating

ASTM D-2843

%

3.4

Flammability

UL 94

HB

Deflection Temperature @ 66 psi (0.45 MPa)

ASTM D-648

°F

207

Smoke Developed Index

ASTM E-84

550

Thermal Conductivity

ASTM C-177

BTU-ft/(hr-ft2-°F)

0.075

Melt Flow Rate

ASTM D-1238

g/10 min.

1.5

Maximum Recommended Continuous Service Temperature

°F

170-190

Softening Temperature

°F

210-220

Chemical

TEST METHOD

UNITS

OPTIX Patterned Acrylic

Resistance to Stress - Critical Crazing Stress to: Solvesso 100

ARTC Modification of MIL-P6997

psi

1,600

Resistance to Stress - Critical Crazing Stress to: Isopropyl Alcohol

ARTC Modification of MIL-P6997

psi

900

Resistance to Stress - Critical Crazing Stress to: Toluene

ARTC Modification of MIL-P6997

psi

1,300

Resistance to Stress - Critical Crazing Stress to: Lacquer Thinner

ARTC Modification of MIL-P6997

psi

500

Mechanical

TEST METHOD

UNITS

OPTIX Patterned Acrylic

Abrasion Resistance - Change in Haze - 200 cycles

ASTM D-1044

Haze, %

24.9

Tensile Modulus of Elasticity

--

psi

490,000

Flexural Strength

ASTM D-790

psi

17,000

Rockwell Hardness

ASTM D-785

M-95

Tensile Impact Strength

ASTM D-1822

ft-lb/in2

20

Izod Impact Strength – Molded Notch

ASTM D-256

ft-lb/in Notch

0.4

Tensile Elongation – Max.

ASTM D-638

%

5.8

Tensile Strength

ASTM D-638

psi

11,030

Abrasion Resistance - Change in Haze - 0 cycles

ASTM D-1044

Haze, %

0

Abrasion Resistance - Change in Haze - 10 cycles

ASTM D-1044

Haze, %

11.2

Flexural Modulus of Elasticity

ASTM D-790

psi

490,000

Izod Impact Strength – Milled Notch

ASTM D-256

ft-lb/in Notch

0.28

Abrasion Resistance - Change in Haze - 50 cycles

ASTM D-1044

Haze, %

24

Physical

TEST METHOD

UNITS

OPTIX Patterned Acrylic

Sound Transmission

ASTM E90 / E413

db

27

Mold Shrinkage

ASTM D-955

mils/in

2-6

Specific Gravity/Relative Density

ASTM D-792

1.19

Optical Refractive Index

ASTM D-542

1.49

Water Absorption

ASTM D-570

% By wt

0.4

Download

**Applicable to the acrylic substrate

These suggestions and data are based on information we believe to be reliable. They are offered in good faith, but without guarantee, as conditions and methods of use are beyond our control. We recommend that the prospective user determine the suitability of our materials and suggestions before adopting them on a commercial scale.